Decorative coating "Roman stone", 7 kg

properties. With virtually no smell, non -toxic, fire -free, environmentally friendly material.

appearance. Gray thick pasta.

Consumption. 1-2 kg/m2 (depending on the application method).

Composition. Latex acrylic, functional additives, thickening, mineral fillers, pigment, water.

storage and transportation. In a closed original package at a temperature of +5 ° C to +30 ° C. Possible storage and transportation at a temperature of up to -20 ° C are no more than one month.

conditions of application. The air temperature and the processed surface from +5 ° C to +35 ° C.

Tool. Kelma made of stainless steel, a spatula.

the drying time. 24 hours.

surface preparation. The basis for applying the material should be perfectly smooth. The surface of the base should be well dried, not to have inseparably holding and shallowing areas, leveled using a finish putty. The prepared surface is treated with a “optimist” with a deep penetration or penetrating, and then a primer covering 100 Optimist -elite.

tinting. For this method of application, the material is tinted in the mass.

application. The first layer of the material is applied to the thickness of the filler. In order to avoid the appearance of visible joints, it is not recommended to leave straight boundaries between the sites. The drying time is 4-6 hours.

The second layer is applied similarly to the first. Dry the coating for 5-10 minutes. After that, the surface with effort is smoothed out by the cell.

Rous the coating with a spatula, trying to hold the tool perpendicular to the surface to achieve the effect of the “vein”. Immediately after this, it is necessary to invite the surface by the edge of the cell along the figure.

After 10-30 minutes, the surface is processed with a valme by “ironing” to give the coating a finished form.